Sic Ceramic Reticulated Foam Filter for Metal Foundry
Product Description
Silicon Carbide Ceramic Foam Filter are just developed as a new type molten metal filter to decrease casting flaw in recent years. With its characteristics of light-weight, high mechanical strength, large specific surface areas, high porosity, excellent thermal shock resistance, erode resistance, high-performance, SIC Ceramic Foam filter is designed for filtering impurities from molten Iron & Alloy, nodular cast iron castings, grey iron castings and malleable castings, Bronze casting, etc. With their excellent resistance to attack and corrosion from molten iron liquid, SIC Ceramic Foam filter can effectively remove inclusions, reduce trapped gas from liquid metal and provide laminar flow, and then the filtered metal is significantly cleaner. Cleaner metal results in higher-quality castings, less scrap, and fewer inclusion defects, all of which contribute to bottom-line profit. Sic ceramic foam filter is designed for filtering impurities from molten Iron & Alloy, nodular cast iron castings, grey iron castings and malleable castings, Bronze casting, etc. It can effectively remove inclusions, reduce trapped gas from liquid metal and provide laminar flow when applied as filter in gating system. We can offer various shapes, such as square, round and custom geometric shapes, Sizes from 10mm up to 600mm, and thicknesses from 10-50mm. The most common porosities are 10ppi, 20ppi, 30ppi, 40ppi, 50ppi, 60ppi. We also can be customized as per client's requirements. SiC ceramic foam filter work at 1500 degree centigrade, apply for iron, copper and copper alloy foundry.
The size are available in square, round and custom geometric shapes; Sizes ranging from 10mm up to 600mm, and thicknesses from 10-50mm. The most common porosities are 10ppi, 15ppi, 20ppi, 25ppi. Higher porosities are available upon request. Custom-made cut-to-size filters are also possible.
Technical specification:
Materia: Silicon Carbide
Color: Grey-black
Applied Temperature: ≤ 1500 Degree C
Pore Size: 8-50 PPI
Porosity: 80-90%
Bulk Density: 0.45-0.55 g/cm3
Compressive strength: ≥ 1.0 MPa
Ceramic foam filters help to enhanced quality of castings and reduce cost.
*Reduce defective rate of castings.
*Improve mechanical properties of castings.
*Reduced costs of finishing operations.
*Simplify pouring systems and increase utilization ratio of mold.
The size are available in square, round and custom geometric shapes; Sizes ranging from 10mm up to 600mm, and thicknesses from 10-50mm. The most common porosities are 10ppi, 15ppi, 20ppi, 25ppi. Higher porosities are available upon request. Custom-made cut-to-size filters are also possible.
Technical specification:
Materia: Silicon Carbide
Color: Grey-black
Applied Temperature: ≤ 1500 Degree C
Pore Size: 8-50 PPI
Porosity: 80-90%
Bulk Density: 0.45-0.55 g/cm3
Compressive strength: ≥ 1.0 MPa
Ceramic foam filters help to enhanced quality of castings and reduce cost.
*Reduce defective rate of castings.
*Improve mechanical properties of castings.
*Reduced costs of finishing operations.
*Simplify pouring systems and increase utilization ratio of mold.
| Chemical Composition | Content |
| Sic | ≥ 70.00% |
| Al 2 O 3 | ≤ 25.00% |
| Other | ≤ 5% |
| Material | Silicon Carbon |
| Operating temperature | ≤ 1500 Degree C |
| Color | Grey black |
| Aperture | 10-60PPI |
| Density | 0.45-0.65g/cm 3 |
| Cell-opening ratio | 80-90% |
| Compressive Strength | ≥ 1.0Mpa |
| Thermal Shock Resistance(1100-2 0Degree C ) | >6 times |
| Application | Molten Iron and its alloys |
| No. | Size (mm) | Porosity | Pore Size (PPI) | Flow velocity (Kg/s) | Filter capacity (Kg) | ||
| Gray cast iron | Ductile cast iron | Gray cast iron | Ductile cast iron | ||||
| 1 | 30 × 50 × 22 | 80-90% | 10-30 | 2-4 | 1-3 | 45-60 | 15-30 |
| 2 | 40 × 40 × 11 | 80-90% | 10-30 | 2-4 | 1-3 | 45-60 | 15-30 |
| 40 × 40 × 13 | 80-90% | 10-30 | 2-4 | 1-3 | 45-60 | 15-30 | |
| 40 × 40 × 22 | 80-90% | 10-30 | 2-4 | 1-3 | 45-60 | 15-30 | |
| 3 | 50 × 50 × 13 | 80-90% | 10-30 | 3-6 | 2-4 | 55-90 | 25-45 |
| 50 × 50 × 22 | 80-90% | 10-30 | 3-6 | 2-4 | 55-90 | 25-45 | |
| 4 | 60 × 60 × 22 | 80-90% | 10-30 | 4-8 | 3-5 | 65-110 | 40-75 |
| 5 | 66 × 66 × 22 | 80-90% | 10-30 | 5-9 | 4-6 | 80-130 | 45-80 |
| 6 | 75 × 50 × 22 | 80-90% | 10-30 | 4-8 | 5-7 | 65-110 | 40-75 |
| 7 | 75 × 75 × 22 | 80-90% | 10-30 | 9-14 | 6-9 | 145-220 | 70-100 |
| 8 | Φ 50 × 22 | 80-90% | 10-30 | 3-5 | 1-3 | 50-70 | 20-40 |
| 9 | Φ 60 × 22 | 80-90% | 10-30 | 3-6 | 2-4 | 65-110 | 35-60 |
| 10 | Φ 70 × 22 | 80-90% | 10-30 | 4-8 | 3-6 | 75-130 | 40-75 |
| 11 | Φ 76 × 22 | 80-90% | 10-30 | 5-9 | 4-7 | 90-150 | 45-80 |
| 12 | Φ 90 × 22 | 80-90% | 10-30 | 10-15 | 6-9 | 180-260 | 75-110 |
| 13 | 100 × 50 × 22 | 80-90% | 10-30 | 8-12 | 5-8 | 130-200 | 65-90 |
| 14 | 100 × 60 × 22 | 80-90% | 10-30 | 9-14 | 6-9 | 180-260 | 70-100 |
| 15 | 150 × 100 × 22 | 80-90% | 10-30 | 18-25 | 12-16 | 300- 400 | 150-210 |
| 16 | 150 × 150 × 22 | 80-90% | 10-30 | 35-50 | 24-36 | 400- 900 | 300-450 |