Sic/Alumina/Zirconia Ceramic Foam Filter
Product Description
Ceramic Foam Filter, remove metal slag and solution of metal impurities are far
stronger than several of the other filters, filter them with a combination of physics
and chemistry. Large inclusions in the filter surface is the physical screen, interception
and tiny inclusions in the role of chemical affinity and be attracted to the filter surface,
side walls or pores. Therefore, to effectively filter out impurities of various sizes,
including much smaller than the pores of the filter impurities. Such filters and comb
the whole disordered molten metal flow, reducing turbulence, allows the molten metal
flow to be smooth and clean.
Ceramic Foam Filter Classification
In accordance with its material, ceramic foam filter can be divided into Silicon Carbide Ceramic
Foam Filter, Alumina Ceramic Foam Filter and Zirconia Ceramic Foam Filter.
Foam Ceramic Filters Working Principle
stronger than several of the other filters, filter them with a combination of physics
and chemistry. Large inclusions in the filter surface is the physical screen, interception
and tiny inclusions in the role of chemical affinity and be attracted to the filter surface,
side walls or pores. Therefore, to effectively filter out impurities of various sizes,
including much smaller than the pores of the filter impurities. Such filters and comb
the whole disordered molten metal flow, reducing turbulence, allows the molten metal
flow to be smooth and clean.
Ceramic Foam Filter Classification
In accordance with its material, ceramic foam filter can be divided into Silicon Carbide Ceramic
Foam Filter, Alumina Ceramic Foam Filter and Zirconia Ceramic Foam Filter.
Foam Ceramic Filters Working Principle
| Material | Alumina Ceramic Foam Filter | Silicon Carbide Ceramic Foam Filter | Zirconia Ceramic Foam Filter |
| Cell Density | 8-60ppi | 8-60ppi | 8-60ppi |
| Opening Rate | 80-90% | 80-90% | 80-90% |
| Temperature | ≤1100celsius degree | ≤1500celsius degree | ≤1700celsius degree |
| Bending Strength At Room Temperature | >0.6Mpa | >0.8Mpa | >1.0Mpa |
| Compressive Strength At Room Temperature | >0.8Mpa | >0.9Mpa | >1.2Mpa |
| Bulk Density | 0.3-0.45g/cm3 | 0.3-0.5g/cm3 | 0.9-1.5g/cm3 |
| Thermal Stability | 6times/1100celsius degree | 6times/1100celsius degree | 6times/1100celsius degree |
| Application | Aluminum, Aluminum Alloys And Other Non-ferrous Alloys | Ductile Iron, Malleable Iron, Gray Iron And Other Iron | Steel, Alloy Seel, Stainless Steel And Other High-melting Metal Alloy |