Customized Alumina Ceramic Foam Filter for Metal Filtration
Product Description
Ceramic Honeycomb Filter is applied to metal liqiud filtration with high achievable surface areas, low thermal expansion, excellent thermal shock resistance and high compressive strength. Ceramic Honeycomb Filter is kind of structural ceramics, with insulation resistance, voltage resistance, high strength, good thermal conductivity, dielectric loss, stable electrical performance characteristics. It is used in electronic ceramic substrates, ceramic electrical insulation, vacuum devices, devices porcelain, spark plugs and other products.
Ceramic honeycomb Filter for the metal melting now is extensively applied to the metallurgic plants of casting/foundry, for example, steel, iron, copper and aluminum, etc. Because of its high mechanical intensity and heat-resistance, it is used to get rid of the metal impurity, refractory scrap, solid refractory alloy, sinter, in the molten metal liquid when casting the products, so as to reduce the air vent of casting, improve the quality of casting and also reduce the casting cost.
Functions:
*Purifying the metal liquid, absorbing the oxide and filtering the non-metal impurities
*Making the metal liquid flowing at stable speed, reducing the vortex and reducing the bubbles in the cast part
*Equalizing the phase structure and prolonging the tools lifetime
*Improving the cast part surface performance and improving the density of the cast part
Ceramic honeycomb Filter for the metal melting now is extensively applied to the metallurgic plants of casting/foundry, for example, steel, iron, copper and aluminum, etc. Because of its high mechanical intensity and heat-resistance, it is used to get rid of the metal impurity, refractory scrap, solid refractory alloy, sinter, in the molten metal liquid when casting the products, so as to reduce the air vent of casting, improve the quality of casting and also reduce the casting cost.
Functions:
*Purifying the metal liquid, absorbing the oxide and filtering the non-metal impurities
*Making the metal liquid flowing at stable speed, reducing the vortex and reducing the bubbles in the cast part
*Equalizing the phase structure and prolonging the tools lifetime
*Improving the cast part surface performance and improving the density of the cast part
| Item | Value | Test Method | |
| Chemical Composition (%) | Al2O3 | ≥90% | Chemical titration |
| SiO2 | ≤8% | Gravimetric Method | |
| Other | ≤2% | Chemical Titration | |
| Compressive Strength (Mpa) | A axis | ≥2.2 | Universal Material Testing Machine |
| B axis | ≥2.5 | ||
| C axis | ≥0.18 | ||
| Water Absorption (%) | 18.5±2 | Gravimetric Method | |
| Softening Temperature (celsius degree) | ≥1380 | High-temperature Electric Resistance Furnace | |
| Thermal Coefficient of Expansion (room temperature ~800celsius degree) (cm/cm/celsius degree) | ≤5.7x10-6 | Expansion Indicator NETZSCH DIL 402PC | |
| Thermal Shock Resistance (room temperature ~650celsius degree) | 650celsius degree 20 minutes/cycle, five cycles no cracking | Air Cooling | |